XLPE Compound

XLPE Compound for MV Power Cable Insulation 1) melt extrusion temperature (116-132) are recommended 2)for cable up to 35kv

No.	Experiment Item		Testing Method	Unit	Typical value
1	Density		GB/T1033-86	g/cm3	0.921
2	Tensile strength		GB/T1040-92	MPa	23
3	Elongation at break		GB/T1040-92	%	530
4	Hot set elongation 0.2 MPa 15min	Elongation under load		%	55
		Permanent deformation after cooling		%	-2
5	Aging  135ºC ,168h	Change of tensile properties		%	9
		Change of elongation properties		%	5
6	Gel content			%	85
7	Brittle temperature -76ºC		GB/T 5470	PC	0
8	Resistance to environmental stress cracking			h	1200
9	Dielectric constant 20°C,50HZ		GB/T 1409-88	/	2.20
10	Dissipation factor 20°C,50HZ		GB/T 1409-88	/	2×10-4
11	DC Volume resistivity 20°C		GB/T 1410-89	Ω·m	9×1014
12	Dielectric strength 20°C		GB/T 1408.1	MV/m	39

YJ-35 XLPE cable insulation material is required to meet the strict standard in the cleaning aspect. In the overall production process, loading, processing and packaging are all strictly controlled; and the overall process is performed in a confined environment. The sample is tested by laboratory impurity detector in the production process periodically, and the impurity content of 1 kg-sampling complies with the following requirements:The impurity particles with 0.175~0.250mm diameter no more than 5; maximum  allowable  in  0.250mm.

Over a broad range of processing technique, YJ-35 can still provide excellent extrusion capacity and smooth surface. For optimum results, melt extrusion temperature in the range of 116 °Cto 132 °C are recommended. For further details, please contact our merchandiser.

 Keep away from sunshine and rain during the transport, and store in clean, dry and ventilated warehouse. The product may be stored for up to 6 months without opening at normal temperature.

XLPE Compound