101CB Silane XLPE Compound

Silane XLPE Compound 1) silane XLPE to insulate the conductor (below 6sqmm) cross-section 2)extrude fast with smooth surface

No.	Experiment Item		Test Method	Unit	Typical Value
1	Tensile strength		GB/T 1040	MPa	24
2	Elongation at break		GB/T 1040	%	450
3	Brittleness temperature -76°C,30pieces		GB/T 5470	pc	0
4	Aging  135°C,168h	Change of tensile strength	GB/T 2951.2-1997	%	+5
		Change of elongation at break		%	-3
5	Thermal extension 200°C,0.2MPa, 15min	Elongation under load	GB/T 2951.5-1997/ GB/T 1040	%	50
		Permanent deformation after cooling		%	0
6	Gel content		JB/T 10437-2004	%	65
7	Dielectric constant 50HZ, 20°C		GB/T 1409		2.2
8	Dielectric loss factor 50Hz, 20 °C		GB/T 1409		3×10-4
9	DC Volume resistivity 20 °C		GB/T 1410	Ω.m	1.0×1015
10	Dielectric strength		GB/T 1408.1-1999	MV/m	38

Silane XLPE Compound used as insulation for low voltage power cables up to 3KV.

It is a type of warm water cross linking insulation material applied for low voltage (up to 3kV) wires 

and cables .

101B is for silane XLPE to insulate the conductor (below 6sqmm) cross-section, extrude fast with smooth surface, and adopt appropriate action to avoid material inner-stress to pass the cable test.

Melt extrusion temperatures in the range of 150°C-220°C are recommended,head of the machine (150°C -220°C ),body of the machine(150°C -200°C) , the specific temperature should be adjusted by actual operation condition.

Keep away from sunshine, rain and soaking during transport. Store in the clean, dry and ventilated warehouses; Storage temperature (minimum:0°C).

Valid period is 6 month while it must be used out in 8 hours after the inner packaging is opened.

101CB Silane XLPE Compound