101B Silane XLPE Compound

101B Silane XLPE Compound
Product Detailed
Related Categories:Other Plastic Raw Materials
Silane XLPE Compound 1) to insulate the conductor (below 6sqmm) cross-section 2)extrude fast with smooth surface

No.

Experiment Item

Test Method

Unit

Typical Value

1

Tensile strength

GB/T 1040

MPa

24

2

Elongation at break

GB/T 1040

%

450

3

Brittleness temperature

-76°C,30pieces

GB/T 5470

pc

0

4

Aging 

135°C,168h

Change of tensile strength 

GB/T 2951.2-1997

%

+5

Change of elongation at break 

%

-3

5

Thermal extension

200°C,0.2MPa, 15min 

Elongation under load

GB/T 2951.5-1997/ GB/T 1040

%

50

Permanent deformation after cooling

%

0

6

Gel content

JB/T 10437-2004

%

65

7

Dielectric constant 50HZ, 20°C

GB/T 1409

2.2

8

Dielectric loss factor 50Hz, 20 °C

GB/T 1409

3×10-4

9

DC Volume resistivity 20 °C

GB/T 1410

Ω.m

1.0×1015

10

Dielectric strength

GB/T 1408.1-1999

MV/m

38

Silane XLPE Compound used as insulation for low voltage power cables up to 3KV.

It is a type of warm water cross linking insulation material applied for low voltage (up to 3kV) wires 

and cables .

101B is for silane XLPE to insulate the conductor (below 6sqmm) cross-section, extrude fast with smooth surface, and adopt appropriate action to avoid material inner-stress to pass the cable test.

Melt extrusion temperatures in the range of 150°C-220°C are recommended,head of the machine (150°C -220°C ),body of the machine(150°C -200°C) , the specific temperature should be adjusted by actual operation condition.

Keep away from sunshine, rain and soaking during transport. Store in the clean, dry and ventilated warehouses; Storage temperature (minimum:0°C).

Valid period is 6 month while it must be used out in 8 hours after the inner packaging is opened.